TI: Particle Aggregation During Fe(III) Bioreduction in Nontronite
AU: * Jaisi, D P
EM:
AF: Department of Geology, Miami University, Oxford, OH 45056 United States
AU: Dong, H
EM: dongh@muohio.edu
AF: Department of Geology, Miami University, Oxford, OH 45056 United States
AU: Hi, Z
EM: he.74@osu.edu
AF: Civil and Environmental Engineering, Ohio State University, Columbus, OH 43210 United States
AU: Kim, J
EM: jinwook.kim@nrlssc.navy.mil
AF: Naval Research Laboratory, NASA Stennis Space Center, Code 7430, MS 39529 United States
AB: This study was performed to evaluate the rate and mechanism of particle aggregation during bacterial Fe (III) reduction in different size fractions of nontronite and to investigate the role of different factors contributing to particle aggregation. To achieve this goal, microbial Fe(III) reduction experiments were performed with lactate as an electron donor, Fe(III) in nontronite as an electron acceptor, and AQDS as an electron shuttle in bicarbonate buffer using Shewanella putrefaceins CN32. These experiments were performed with and without Na- pyrophosphate as a dispersant in four size fractions of nontronite (0.12-0.22, 0.41-0.69, 0.73-0.96 and 1.42-1.8 mm). The rate of nontronite aggregation during the Fe(III) bioreduction was measured by analyzing particle size distribution using photon correlation spectroscopy (PCS) and SEM images analysis. Similarly, the changes in particle morphology during particle aggregation were determined by analyses of SEM images. Changes in particle surface charge were measured with electrophoretic mobility analyzer. The protein and carbohydrate fraction of EPS produced by cells during Fe(III) bioreduction was measured using Bradford and phenol-sulfuric acid extraction method, respectively. In the presence of the dispersant, the extent of Fe(III) bioreduction was 11.5-12.2% within the first 56 hours of the experiment. There was no measurable particle aggregation in control experiments. The PCS measurements showed that the increase in the effective diameter (95% percentile) was by a factor of 3.1 and 1.9 for particle size of 0.12-0.22 mm and 1.42-1.80 mm, respectively. The SEM image analyses also gave the similar magnitude of increase in particle size. In the absence of the dispersant, the extent of Fe(III) bioreduction was 13.4-14.5% in 56 hours of the experiment. The rate of aggregation was higher than that in the presence of the dispersant. The increase in the effective diameter (95% percentile) was by a factor of 13.6 and 4.1 for the particles size of 0.12-0.22 and 1.42-1.8 mm, respectively. The particle aggregation was limited in control experiment to the factor of 2.8 and 2.1 for these two size fractions, respectively. The measured electrophoretic mobility decreased with increase in the extent of bioreduction and aggregation, but the rate of decrease was greatest in the finest size fraction. The EPS measurements showed the increase in the carbohydrate and protein fractions as a result of bioreduction. Separate experiments were performed to understand the relative contribution of Fe(III) reduction and EPS production in controlling nontronite particle aggregation The rate of particle aggregation was measured for nontronite that was chemically pre-reduced by dithionite to various extents, both with and without addition of dextran, a neutral and pure EPS. The aggregation rate was greater in the nontronite that were pre-reduced to a higher extent than those with a lower extent of reduction. The relative contribution to particle aggregation due to Fe(III) reduction and polysaccharide bridging was about 4:1. However, in the real system where bacterial cells are involved, and amount of EPS production and extent of Fe(III) bioreduction increase with time, the relative contribution may be different than in this simple system. In summary, we conclude that both Fe(III) reduction and microbial production of EPS contribute to the observed nontronite particle aggregation with Fe(III) reduction playing more dominant role.